Elucidating the Roles of Redox and Structure in the Grain Growth of Mn-doped UO2

Abstract Mn-doped UO2 is considered a potential advanced nuclear fuel due to ameliorated microstructural grain growth compared to non-doped variants. However, recent experimental investigations have highlighted limitations in growth mechanisms, apparently arising from misunderstandings of its redox-structural chemistry. To resolve this disparity, this investigation has used a combination of synchrotron X-ray diffraction and spectroscopy measurements supported by ab initio calculations to cross-examine the redox and structure chemistry of Mn-doped UO2 single crystal grains and ceramic specimens. Mn was found to enter the UO2 matrix divalently with additional formation of fluorite Mn+ 2O in the bulk material. Extended X-ray absorption near edge structure measurements indicated that due to the isostructural fluorite relationship between UO2 and Mn+ 2O, grain enhancing diffusing U species, that should migrate to neighbour UO2 grains during sintering, are inadvertently incorporating within MnO, inhibiting grain growth. The investigation consequently highlights the significance of considering total redox and structural chemistry of main and minor phases in the design of advanced materials.