High value-added utilization of desulfurized building gypsum as self-leveling mortar: the comprehensive effect of cement
preprint
OA: closed
Abstract
Abstract The utilization of desulfurized building gypsum as raw material for gypsum-based self-leveling mortar (GSL) is limited by its low strength and poor water resistance. The objective of this study was to improve comprehensive properties of GSL and prepare qualified desulfurized building gypsum-based self-leveling mortar, which had been applied in practical engineering. The influence of cement on water consumption rate of initial fluidity (W/M ratio), fluidity, setting time, mechanical strength, and water resistance of GSL were evaluated. Besides, the rheological parameter, heat of hydration, crystal morphology, and pore structure were also analyzed. Cement greatly improved the fluidity of slurry. Moreover, the compressive strength and softening coefficient of GSL reached 20.6 MPa and 0.56 at 10% cement, respectively. Cement reduced the 30 min-fluidity loss and improved fludity by reducing the yield stress and increasing the plastic viscosity of screed. The transformation of hydration kinetics of GSL could be due to Ca2+ and OH− released by cement, thus resulting in the shortening of initial setting time and the prolongation of the interval between initial and final setting time. Scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS) showed that CSH gel and AFt crystal would generate on the surface of CaSO4·2H2O crystal, making the structure more compact. Mercury Intrusion porosimetry (MIP) indicated that cement greatly reduced the porosity through the water reduction effect in the early stage and continuous hydration in the later stage. The continuous hydration of cement also increased the shrinkage rate. This work was expected to provide reference for promoting the application of desulfurized building gypsum as the high value-added screed.
My notes (saved in your browser only)
Citation neighborhood (no data yet)
We don't have any in-corpus citations linked to this paper yet. The paper's references may be in our DB but unresolved to ``paper_id`` (resolution happens at ingest when the cited DOI matches a row we already have). Run the cross-source citation reconcile pass to retry.
References (27)
- doi:10.1016/j.jclepro.2016.04.054 via crossref
- doi:10.1016/j.cemconcomp.2022.104714 via crossref
- doi:10.1016/j.psep.2023.02.040 via crossref
- doi:10.1016/j.rser.2021.111931 via crossref
- doi:10.1016/j.conbuildmat.2018.02.101 via crossref
- doi:10.3390/ma15072680 via crossref
- doi:10.1016/j.jclepro.2018.01.002 via crossref
- doi:10.1016/j.cemconcomp.2008.06.004 via crossref
- doi:10.1016/j.conbuildmat.2020.118198 via crossref
- doi:10.1016/s0008-8846(03)00233-3 via crossref
- doi:10.1016/j.conbuildmat.2018.09.110 via crossref
- doi:10.1016/j.envpol.2021.117799 via crossref
- doi:10.1016/j.jclepro.2018.05.228 via crossref
- doi:10.1016/j.cemconcomp.2016.02.007 via crossref
- doi:10.1016/j.cemconres.2017.08.026 via crossref
- doi:10.1016/j.esr.2020.100458 via crossref
- doi:10.1016/j.enbuild.2018.11.023 via crossref
- doi:10.1016/j.jclepro.2020.120056 via crossref
- doi:10.1016/j.jclepro.2017.08.049 via crossref
- doi:10.1016/j.conbuildmat.2021.124982 via crossref
- doi:10.1007/s10973-018-7825-3 via crossref
- doi:10.1016/j.conbuildmat.2019.07.289 via crossref
- doi:10.1016/j.conbuildmat.2016.12.206 via crossref
- doi:10.1016/j.cemconres.2015.03.013 via crossref
- doi:10.1016/j.cemconres.2018.04.008 via crossref
- doi:10.1016/0008-8846(96)00064-6 via crossref
- doi:10.1016/j.conbuildmat.2021.123775 via crossref
Source provenance
- crossref
- last seen: 2026-05-21T01:00:30.344985+00:00
- europepmc
- last seen: 2026-05-20T01:45:00.602351+00:00