Micro-Particles of High Entropy Alloys Made by Laser Induced Forward Transfer

Controlled deposition of CoCrFeNiMo0.2 high entropy alloy (HEA) micro-particles was achieved using laser induced forward transfer (LIFT). Ultra-short laser pulses, 230 fs of 515 nm wavelength, were tightly focused into ∼ 2.4 μm focal spots on the ∼50 nm thick plasma-sputtered films of CoCrFeNiMo0.2. The HTA films were transferred onto glass substrates by magnetron sputtering in vacuum (10−8 atm) from the thermal spray coated substrates. The absorption coefficient of CoCrFeNiMo0.2 α ≈ 6 × 105 cm−1 was determined at 600 nm wavelength. The real and imaginary parts of refractive index (n + iκ) of HEA were determined from reflectance and transmittance using nano-films.