Optimizing the conductivity, microstructure and mechanical properties of tape-cast LATP with LiF and SiO2 additives

Abstract LATP sheets with LiF and SiO2 addition prepared by tape casting as electrolytes for solid-state batteries were characterized regarding conductivity, microstructure and mechanical properties aiming towards an optimized composition. The use of additives permitted a lowering of the sintering temperature. As general trend, higher LiF to SiO2 ratios led to lower porosities. This decrease in the porosity corresponds to an increase of the ionic conductivity as well as higher values of elastic modulus and hardness determined by indentation testing. Micro-pillar testing was used to assess the crack growth behavior, revealing weak grain boundaries.