Effects of Heat Treatment on the Microstructure and Mechanical Properties of a Dual-Phase High-Entropy Alloy Fabricated via Selective Laser Melting

To enhance the applicability of dual-phase high-entropy alloys (HEAs) like Fe32Cr33Ni29Al3Ti3, fabricated via selective laser melting (SLM), a focus on improving their mechanical properties is essential. As part of this effort, heat treatment was explored. This study compares the microstructure and mechanical properties of the as-printed sample with those cooled in water after undergoing heat treatment at temperatures ranging from 1000 to 1200 ℃ for 1 hour. Both pre- and post-treatment samples reveal a dual-phase microstructure comprising FCC and BCC phases. Although heat treatment led to a reduction in tensile and yield strength, it significantly increased ductility compared to the as-printed sample. This strength-ductility trade-off is related to changes in grain sizes with ultrafine grains enhancing strength and micron grains optimizing ductility, also the influence of the content of FCC/BCC phases and dislocation density. In particular, the sample heat-treated at 1000 °C for 1 hour and then water-cooled exhibited a better combination of strength and ductility, a yield strength of 790 MPa, and an elongation of 13%. This research offers innovative perspectives on crafting dual-phase HEA of Fe32Cr33Ni29Al3Ti3, allowing for tailorable microstructure and mechanical properties through a synergistic approach involving SLM and heat treatment.