Applying MICP Technology to Improve the Bond Strength of LWAC after High-Temperature Damage

This study aimed to use biomineralization technology to improve the bond strength of fiber-reinforced lightweight aggregate concrete (LWAC) after exposure to temperatures of 300 °C and 500 °C. The specimens of a control group (Group A) and two experimental groups (Group B and Group C) were prepared. These specimens healed themselves in different ways after exposure to high temperatures and pull-out tests. The self-healing method of Group A involved placing the specimen into an incubator. The self-healing method of Group B was the same as that of Group A. The self-healing method of Group C involved immersing the specimen in a mixed solution of urea and calcium acetate for two days, then taking it out and placing it in an incubator for two days. A cycle of four days was undertaken until the desired age was reached. After the specimens were healed to the planned age, the first and secondary pull-out tests and repair compound identification were carried out. After exposure to a temperature of 300 °C and self-healing for 90 days, compared with the specimens in Group A, the relative bond strength ratios of the secondary pull-out tests of the specimens in Group C increased by 20.3%. This indicates that biomineralization can effectively improve the bond strength of LWAC after high-temperature damage.