Transferable, Transparent and Flexible Pseudocapacitors from Ternary V2O5/PEDOT/Graphene Electrodes with High Durability in Organic Electrolyte

Transparent conductive electrodes (TCEs) are of enormous significance to the emergence of flexible and wearable electronics and continued growth of modern devices. Versatile and tunable TCEs, featuring with not only high optical transmittance but also intriguing features of electrochemical energy-storage capability, remain a significant challenge. Here we develop capacitive active films comprised of graphene-conjugated V2O5@poly (3,4-ethylene dioxythiophene) ternary composite (V2O5@PEDOT/rGO) on silver nanowire coated substrates as solid-state super/pseudocapacitors. The constructed electrodes exhibit improved electrolyte ions interaction with effective graphene layer, achieving high areal capacitance 0.6-1.2 mF.cm−2 with 0.5M LiCl electrolytes at optical transparency >60% with record durability. As demonstrated, the kinetic blocking of PEDOT layer and anchoring capability of graphene upon amphoteric soluble vanadium ions from layered V2O5 nanoribbons/nanobelts contribute synergistically to the unusual electrochemical stability, also shown using scanning electrochemical microscopy (SECM) providing electroactivity sites and ion transportation rates. As-fabricated symmetric solid-state supercapacitors delivered broad potential window >1.4 V under two different electrolyte environments (aqueous LiCl and LiCl/PVA gel) and demonstrated higher power and energy density (0.27 μWh.cm−2) outperforming previously reported devices at <0.1 μWh.cm−2. The electrochemical properties are also discussed in terms of solvation in polymer gel electrolyte ions.